Cold Rolled Polished Stainless Steel Plate 430 420 409L 410 0.15mm - 3mm Polish Thickness
Desprition:
409/409L
Ferritic stainless steel with low C, N contents and addition of Ti, Magnetic;
Low cost and stable price without Ni content;
High thermal conductivity, low coefficient of thermal expansion, good formability and bendability;
Good corrosion resistance and elevated temperature strength;
Unnecessary for heat treatment after welding due to low C and the addition of Ti
Application: Automotive exhaust parts, such as exhaust manifold, catalytic converter, Muffler, etc
Chemical Composition
| Steel Grade | % | |||
| C (max.) | Cr | Ti | Mn (max.) | |
| 409 | 0.03 | 10.0-11.5 | 6*C-0.75 | 1.0 |
Mechanical Properties
| Steel Grade | Y.S (Mpa) | T.S (Mpa) | E.L (%) | Hardness |
| 409 | >175 | >360 | >25 | <80 (HRB) |
410L
Ferritic steel with low C and Cr contents, magnetic, low cost and stable price without Ni content; Good formability, weldability and bendability,; High thermal conductivity and low coefficient of thermal expansion.
Application:
Reefer container, vessel housing, automotive exhaust pipe, Heat exchanger, Boiler combustion chamber, burner component and Nozzle.etc
410S
Representative martensitic stainless steel, low cost and stable price without Ni content, Higher tensile strength and good formability, but not suitable in highly corrosive environment, higher hardness can be attained by heat treatment(magnetic)
Application: Kitchen utensils, cutlery, some mechanical components, etc
Chemical Composition
| Steel Grade | % | ||||
| C (max.) | Cr | Si (max.) | Mn (max.) | ||
| 410L | 0.03 | 11.0-13.50 | 1.0 | 1.0 | |
| 410S | 0.08 | 11.0-13.50 | 1.0 | 1.0 | |
Mechanical Properties
| Steel Grade | Y.S (Mpa) | T.S (Mpa) | E.L (%) | Hardness |
| 410L | >195 | >360 | >22 | <88 (HRB) |
| 4 Cold Rolled Polished Stainless Steel Plate 430 420 409L 410 0.15mm - 3mm Polish Thickness |